Injectable alloplastic implants and methods of use thereof

ABSTRACT

Described herein are injectable alloplastic implant compositions that are particularly useful for soft tissue defect augmentation. The compositions include microparticles, such as polymethylmethacrylate particles, and collagen as a suspending agent, wherein the collagen contains a reduced amount of low molecular weight gelatine compared to high molecular weight collagen. By controlling the molecular weight of the collagen in the compositions, the injectability, stability, and antigenicity of the alloplastic implant compositions can be improved.

CROSS-REFERENCE TO RELATED APPLICATIONS

This application is a continuation of U.S. application Ser. No.14/211,994 filed on Mar. 14, 2014, which is incorporated herein byreference in its entirety.

FIELD OF THE DISCLOSURE

The present disclosure is related to injectable alloplastic implants andmethods of filling defects such as facial defects.

BACKGROUND

Augmentation of soft tissue, e.g., skin, can be employed in manysituations, including recovery from injury and for cosmetic orsupporting purposes. For example, with normal aging, skin may becomeloose or creases can form, including, for example, nasal-labial folds,wrinkles, pitting and defects. Soft tissue augmentation can be used tocorrect defects such as creases and lines, and to counteract the effectsof aging. It is desirable to even out irregularities of the skinpermanently and without side effects. Soft tissue augmentation isachieved by the use of such materials as collagen, silicone, poly-lacticacid, polyethylene, polytetrafluoroethylene, and hydrogel-based polymercompositions. These materials can be in various forms depending on theuse; for example, they can be in the form of thick solutions, gels orsuspensions and used as implants or carriers for delivering theimplants. Ideal materials for soft tissue augmentation should besufficiently durable and remain in position and should not migrate fromthe implantation site.

Injectable dermal fillers are particularly desirable as a noninvasiveintervention for reducing the appearance of skin defects. Injectabledermal fillers raise the skin within the skin defect, which is lower ordeeper than the surrounding skin, causing the defect to fill to the samelevel as the surrounding skin, reducing the visibility of the defect.

U.S. Pat. No. 5,344,452 describes an alloplastic implant that isbiocompatible and remains permanently at the injection site withsubstantially no side effects. The implant composition comprises solidparticles having a smooth surface and being free from corners and edgessuch as a biocompatible solid in powder form, in particular polymethylmethacrylate (PMMA), in the form of microparticles. In certain aspects,the implant composition includes a physiologically acceptable suspendingagent or carrier such as a biodegradable gelatine, water and/or alcohol.Such a dermal filler is commercially available as Artefill®.

While the compositions of U.S. Pat. No. 5,344,452 are well-suited fortheir intended purpose, it is desirable to design implant compositionswith improved physical properties such as injectability and storagestability.

BRIEF SUMMARY

In one aspect, an alloplastic implant composition comprisesmicroparticles having a diameter of about 5 to about 400 μm suspended inan aqueous suspending agent, wherein the aqueous suspending agentcomprises denatured atelocollagen, wherein the denatured atelocollagenhas less than 40 wt % of the total weight as components of weightaverage molecular weight (Mw) 100,000 Daltons or lower.

In another aspect, a method of augmenting a soft tissue defect comprisesinjecting an alloplastic implant composition near the soft tissuedefect, wherein the alloplastic implant composition comprises denaturedatelocollagen that has less than 40 wt % of the total weight ascomponents of weight average molecular weight (Mw) 100,000 Daltons orlower.

In a further aspect, a method of improving the injectability of aninjectable alloplastic implant composition comprises forming theinjectable alloplastic implant composition comprising microparticleshaving a diameter of about 5 to about 400 μm suspended in an aqueoussuspending agent, wherein the aqueous suspending agent comprisesdenatured atelocollagen, wherein the denatured atelocollagen has lessthan 40 wt % of the total weight as components of weight averagemolecular weight (Mw) 100,000 Daltons or lower.

DETAILED DESCRIPTION

Described herein are injectable alloplastic implant compositions thatare particularly useful for soft tissue defect augmentation. In oneaspect, the compositions include collagen. In a specific aspect, thecompositions include microparticles, such as polymethylmethacrylateparticles, and a suspending agent comprising collagen, wherein thecollagen contains a reduced amount of gelatine compared to highmolecular weight collagen. Specifically, the microparticles aresuspended in an aqueous suspending agent which is an aqueous collagensolution. In an embodiment, an alloplastic implant composition comprisesmicroparticles having a diameter of about 5 to about 400 μm suspended inan aqueous suspending agent comprising denatured atelocollagen, whereinthe denatured atelocollagen has less than 40 wt % of the total collagenweight as components of weight average molecular weight (Mw) 100,000Daltons or lower. In one aspect, the denatured atelocollagen has 60 wt %or greater, specifically 60 to 100 wt %, components of weight averagemolecular weight 100 kDa to 258 kDa. Optionally, the polydispersity ofthe denatured atelocollagen expressed as Mw/Mn is 1.0 to 1.6, wherein Mwis weight average molecular weight and Mn is number average molecularweight. It was unexpectedly found that when collagen contains asignificant fraction of low molecular weight gelatine (e.g., less than100 kDa or even much smaller), the resulting implant compositions canhave reduced gel strength as well as reduced storage stability. Inaddition, the low molecular weight gelatine component of the collagencontributes to difficulty in injecting the compositions as noted in thebackground of U.S. Pat. No. 5,344,452. The reduction of the amount ofthe low molecular weight components of the collagen is also expected toreduce the immunological response to the alloplastic implantcompositions that can occur upon injection into a human subject.

Without being held to theory, it is believed that denaturedatelocollagen having 60 wt % or greater components of weight averagemolecular weight 100 kDa or higher as described herein allows forimproved water junction formation and subsequent physical properties foruse in an alloplastic implant that were not previously achieved. Theimproved properties may include, but are not limited to, broad rangetemperature stability, constant flow rheological characteristics,superior microparticle suspending properties, and maintained homogeneousmicroparticle distribution during storage within holding vials and/orsyringe-like delivery vehicles. In certain aspects, the denaturedatelocollagen has less than 40 wt % of the total collagen weight ascomponents of weight average molecular weight (Mw) of less than 80 kDa,less than 60 kDa, less than 40 kDa or less than 20 kDa. In anotheraspect, the denatured atelocollagen has greater than 60% of the totalweight as components of weight average molecular weight (Mw) of greaterthan 120 kDa, 150 kDa, 160 kDa, 175 kDa, 180 kDa or 200 kDa. In a yetfurther aspect, the denatured atelocollagen has less than 30 wt %, 25 wt%, 20 wt %, 15 wt %, 10 wt % or 5 wt % of the total collagen weight ascomponents of weight average molecular weight (Mw) of less than 100 kDa.In a still further aspect, the denatured atelocollagen has 60 wt % orgreater, 70 wt % or greater, 75 wt % or greater, 80 wt % or greater, 85wt % or greater, 90 wt % or greater or 95 wt % or greater, components ofweight average molecular weight 100 kDa to 258 kDa. In one aspect, thedenatured atelocollagen is prepared from bovine or porcine collagen.

As used herein, the term microparticle refers to small particles thathave a substantially smooth surface and that are free from corners,edges and the like. In other words, the particles do not have sharptransitions at their surfaces such as would be found at corners andedges. In addition, the particles do not have peaks or taperedprojections. In one aspect, the surface does not contain pores. Due tothe smooth and smoothed off surface structure, no cells and other tissuestructures are damaged when the microparticles are injected into softtissue. In addition, the danger of causing reactions of the tissue,which are followed by infections, is minimized.

In one aspect, the microparticles are dynamically balanced solidparticles, and in particular particles having an elliptical or sphericalform. In addition, it is possible to use solid particles of differentgeometrical forms if substantially all the particles have a smooth orsmoothed-off surface.

The microparticles have an average diameter of about 5 to about 400 μm,specifically about 10 to about 200 μm, and more specifically about 15 toabout 60 μm. As used herein, the term “about” means±10%. If themicroparticles do not have a spherical form, then the diameter refers tothe greatest diameter of the smallest cross sectional area. Such solidparticles are too large to be “eaten” by monocytes. Due to the form,surface and size of the particles, they are not detected by theendogenous macrophages as foreign bodies, so no defensive reactions takeplace. In addition, the microparticles are small enough to be injectedthrough a cannula of an injection syringe to the desired site.Microparticles having the diameters specified above cannot be identifiedby touch as a single foreign body in or under the skin. Advantageously,the microparticles have a diameter such that they are not washed awaythrough lymph tracts or other tissue tracts from the site to which theyhave been administered. In addition, microparticles having a sphericalform or a spherical-like form have the advantage that they form aclosely packed arrangement at the site where they have been placed.

The microparticles are composed of an inert, histocompatible materialsuch as glass. In another aspect, the solid particles are composed of apolymer, and in particular a completely cured and fully polymerizedpolymer so that no remaining monomers, which may be toxic or may causecancer, are incorporated into the body of the treated patient. It ispossible to use any inert histocompatible polymer/copolymer forproducing the microparticles.

Exemplary polymers include substituted and unsubstitutedpolymethyacrylates, sodium acrylate polymers, acrylamide polymers,acrylamide derivative polymer or copolymers, sodium acrylate and vinylalcohol copolymers, vinyl acetate and acrylic acid ester copolymers,vinyl acetate and methyl maleate copolymers, isobutylene-maleicanhydride crosslinked copolymers, starch-acrylonitrile graft copolymers,crosslinked sodium polyacrylate polymers, crosslinked polyethyleneoxide, acrylate/methacrylate copolymers, and mixtures thereof. In oneembodiment, the microparticles comprise a polymer or copolymercomprising a methacrylate monomer such as a methylmethacrylate monomer.

In one aspect, polymethacrylates and in particularpolymethylmethacrylate (PMMA) is used as the polymer for themicroparticles. Fully polymerized PMMA is histocompatible and ischemically and physically inert in the human body. PMMA is used inmanufacturing implants, for instance for the plastic covering of bonedefects in the face and in the cranium or as an arthroplasty. PMMA isalso used for the manufacturing artificial teeth, as suture material andfor manufacturing intraocular lenses and dialysis membranes.

In order to inject the microparticles as an implant in or under theskin, the microparticles are suspended in an aqueous suspending agent.In one aspect, the aqueous suspending agent has a pH of 6.0 to 8.0, andincludes, for example, a salt such as sodium chloride and a buffer suchas a phosphate buffer. The suspending agent includes denaturedatelocollagen as described herein such as denatured atleocollagen having60 wt % or greater components of weight average molecular weight 100 kDaor higher. In one aspect, the denatured collagen comprises 0.5 to 15 wt% of the suspending agent, specifically 1 to 10 wt %, more specifically3 to 5 wt % and most specifically 3.5 wt % of the suspending agent. Anexemplary suspending agent includes 3.5 wt % denatured atelocollagen,0.3 wt % lidocaine hydrochloride, 2.7 wt % phosphate buffer, 0.9 wt %sodium chloride and 92.6 wt % water for injection.

Collagen, atelocollagen, and gelatine are physically and structurallydifferent and these differences manifest themselves in various physicalproperties that are important when evaluating viable biomaterials thatmay be used as suspending agents for dermal filling and correctivetreatment of tissue defects, such as wrinkles and scars. Collagen is theprimary structural protein of connective tissue in animals and is themost abundant protein in mammals. Collagen is composed of a triple helixwith two identical chains (α1) and a third chain that differs slightlyin its chemical composition (α2). Collagen sequences are well-known inthe art and the most abundant sequences are glycine-proline-X andglycine-X-hydroxyproline. Collagen can be isolated from a variety ofanimal sources and includes, for example, bovine collagen. Collagen alsoincludes recombinant collagen. Atelocollagen is a water-soluble form ofcollagen formed through treatment of collagen with proteases. Gelatineis derived through partial hydrolysis of the collagen extracted fromanimal skin, bones, cartilage, ligaments, etc. Denatured collagen, suchas denatured atelocollagen, refers to substantially single-strandedcollagen, specifically collagen containing greater than 90% singlestrands. Denatured collagen is produced by, for example, alkali-enzymetechniques.

While collagen and gelatine have been used previously in the field ofsoft tissue augmentation, the molecular weight of the collagen andgelatine is rarely identified. In general, intact collagen has amolecular weight distribution including fractions of 100 kDa and below,as well as 200 kDa molecular weight fractions and even 250,000 Daltonmolecular weight fractions. The average molecular weight of collagen isabout 300 kDa, although individual preparations have lower molecularweights due to degradation of the collagen chains, for example.Atelocollagen generally has an average molecular weight of 258 kDa.Irreversible gelatine has an average molecular weight of about 2,000Daltons. Unless indicated otherwise, molecular weight as used hereinrefers to weight average molecular weight.

As noted in the background of U.S. Pat. No. 5,344,452, while gelatine isa biodegradable protein that is useful in compositions to even out skinirregularities, gelatine can be extremely difficult to inject. In theArtefill® product, bovine collagen is used instead of gelatine as it isalso biodegradable and is further easier to inject. However, it has beendiscovered that preparations of collagen such as bovine collagen containa distribution of molecular weights, including a low molecular weightgelatine component. Without being held to theory, it is believed thatthe gelatine component of collagen preparations contributes tochallenges with injection/extrusion force and also causes immunologicalresponses. In order to improve the functionality of the suspending agentto provide improved injectability and extrusion force, improved gelstrength, facilitate room temperature stability, as well as preventmicroparticles from aggregating at temperature elevated above 2-8° C.,the gelatine component of collagen preparations should be eliminated.

The gelatine (i.e., low molecular weight components) can be removed fromcollagen preparations by techniques known in the art such as dialysis orsize exclusion chromatography. In one embodiment, the collagen is bovineor porcine collagen. The collagen an also be crosslinked withglutaraldehyde, including lightly crosslinked collagen.

In addition to the collagen, the aqueous suspending agent can includealcohols such as ethyl alcohol, and/or a tenside such as Tween® 80 aswell as mixtures thereof. Tween® 80 is a polyethoxysorbitanoleate. It isnot only possible to use the mentioned Tween® type (Tween 80) but alsoother Tween® types. The tenside changes the surface tension of water sothat the solid particles and in particular the polymer particles floatbetter.

In another embodiment, the suspending agent further comprises sodiumhyaluronate or crosslinked sodium hyaluronate.

The mixing ratio of the components of the suspending agent can be chosenaccording to the needs and in particular according to the size of thesyringe used for the injection.

In one embodiment, the alloplastic implant composition has improvedstability, for example, the microparticles are stable for at least 30days at a temperature of 20 to 25° C. As used herein, the term stablemeans that the microparticles do not agglomerate and/or aggregate whensuspended in an aqueous dispersion containing the suspending agentdescribed herein. In one aspect, the suspending agent described hereinprovides a stable suspension over a wide range of temperatures, such as2 to 25° C.

By using the suspending agent disclosed herein, it is easier to injectthe solid particles as with the help of an injection syringe, forinstance intracutenously. It is for instance possible to use a 20 to 30gauge, specifically a 26 or 27 gauge needle for such an injection. A 26gauge needle has a 0.45 mm outer diameter, and a 27 gauge needle has a0.4 mm outer diameter.

In another embodiment, a method of improving the injectability of aninjectable alloplastic implant composition comprises forming theinjectable alloplastic implant composition comprising microparticleshaving a diameter of about 5 to about 400 nm suspended in an aqueoussuspending agent, wherein the aqueous suspending agent comprisesdenatured atelocollagen, wherein the denatured atelocollagen has lessthan 40 wt % of the total weight as components of weight averagemolecular weight (Mw) 100,000 Daltons or lower.

One disadvantage of the Artefill® product is that a skin test isrequired prior to use because the product contains bovine collagen andis contraindicated in subjects with allergies to bovine collagenproducts. Without being held to theory, it is believed that because thecollagen used in the alloplastic implant compositions described hereindo not contain the low molecular weight gelatine component, the risk ofan adverse allergic response is reduced. Thus, in one embodiment, a skintest to determine sensitivity to the collagen in the alloplastic implantcomposition is not required prior to use.

The compositions can further include one or more active agents such asone or more local anesthetics such as lidocaine, anti-inflammatoryagents, tissue formation agents, adipose tissue formation agents,anesthetics, antioxidants, heparin, epidermal growth factor,transforming growth factor, transforming growth factor-β,platelet-derived growth factor, fibroblast growth factor, connectivetissue activating peptides, β-thromboglobulin, insulin-like growthfactors, tumor necrosis factors, interleukins, colony stimulatingfactors, erythropoietin, nerve growth factors, interferons orcombinations thereof. Additional active agents includeglucosaminoglycans, fibronectins, lectins, polycations (such polylysine,chitosan and the like), surface receptor binding motifs likearginine-glycine-aspartic acid (RGD), growth factors like basicfibroblast growth factor (bFGF), platelet derived growth factor (PDGF),transforming growth factor (TGF), cytokines like tumor necrosis factor(TNF), interferon (IFN), interleukins (IL), and structural sequencesincluding elastin, hyaluronic acid and others. Additionally recombinant,synthetic, or non-native polymeric compounds might be used as decorationincluding chitin, poly-lactic acid (PLA), and poly-glycolic acid (PGA).Other active agents include tracers, and contrasting agents. Thecompositions can further comprise one or more cells or tissues, such asadipose tissue or dermal fibroblasts. In one aspect, the cells areautologous cells.

In one embodiment, a method of filling a soft tissue defect comprisesinjecting an alloplastic implant composition near the soft tissuedefect, wherein the alloplastic implant composition comprises denaturedatelocollagen that has less than 40 wt % of the total weight ascomponents of weight average molecular weight (Mw) 100,000 Daltons orlower. In one aspect, the denatured atelocollagen is in the form ofsuspending agent and the alloplastic implant composition further hassuspended therein microparticles having a diameter of about 5 to about400 μm.

In certain aspects, the denatured atelocollagen has less than 40 wt % ofthe total collagen weight as components of weight average molecularweight (Mw) of less than 80 kDa, less than 60 kDa, less than 40 kDa orless than 20 kDa. In another aspect, the denatured atelocollagen hasgreater than 60 wt % of the total weight as components of weight averagemolecular weight (Mw) of greater than 120 kDa, 150 kDa, 160 kDa, 175kDa, 180 kDa or 200 kDa. In a yet further aspect, the denaturedatelocollagen has less than 30 wt %, 25 wt %, 20 wt %, 15 wt %, 10 wt %or 5 wt % of the total collagen weight as components of weight averagemolecular weight (Mw) of less than 100 kDa. In a still further aspect,the denatured atelocollagen has 60 wt % or greater, 70 wt % or greater,75 wt % or greater, 80 wt % or greater, 85 wt % or greater, 90 wt % orgreater or 95 wt % or greater, components of weight average molecularweight 100 kDa to 258 kDa. In one aspect, the denatured atelocollagen isprepared from bovine collagen or porcine collagen.

In one embodiment, the alloplastic implant composition as describedherein is injected near a soft tissue defect in a human subject toaugment the soft tissue defect. The alloplastic implant composition maybe injected below the soft tissue defect at a junction of the dermis andsubcutaneous fat to augment soft tissue and to provide long-termreduction of a skin defect. In one aspect, injection is performed usinga tunneling technique in which the needle is moved back and forth belowthe scar. In general, pressure is applied during the entire injectionprocess.

In one aspect, the soft tissue defect is the result of aging includingpremature aging. Aging can be a result of loss of collagen andhyaluronic acid in the skin during the aging process or a result ofpremature aging caused by, for example, overexposure to sunlight,overexposure to environmental pollutants, smoking tobacco products,exposure to cigarette smoke, poor nutrition and/or skin disorders. Inone aspect, the soft tissue defect is a nasolabial fold, also known as“smile lines” or “laugh lines.”

In another embodiment, the soft tissue defect is a wrinkle, such as adynamic wrinkle, a fine wrinkles or a static wrinkle. Dynamic wrinklesinclude a forehead crease, a brow burrow or an eye line (crow's feet).Static wrinkles include skin fold wrinkle resulting from sagging skin.

In another embodiment, the soft tissue defect is a scar such as an acnescar, a “rolling” scar, a “boxcar” scar or an “ice pick” scar, asurgical scar, trauma scar, a large pore and a soft tissue contourdefect.

In another aspect, the soft tissue defect can be caused by a medicalcondition resulting in a deformity that requires re-contouring, such asa small tissue defect (e.g., after animal bite(s)) or a deformityrelated to trauma where the deformity is cosmetically unappealing. In afurther embodiment, augmentation may be after plastic surgery to achievesymmetry or a desired result.

As used herein, a “long-term” reduction of a soft tissue defect is of aduration of at least one year, specifically one year to about fiveyears, more specifically about five years to about ten years, and mostspecifically about ten years or longer.

In one embodiment, injection of the alloplastic implant composition isrepeated at 2 week intervals until the desired level of correction isachieved.

The invention is further illustrated by the following non-limitingexamples.

EXAMPLES Characterization of Collagen

Using laser light scattering in conjunction with an Optilab™ refractiveindex detector and a QELS measurement, soluble collagen was studied todetermine absolute molar mass moments (Mn, Mp, Mw and Mz) thepolydispersity (Mw/Mn and Mz/Mn) the rms radius moments (Rn, Rw and Rz),the hydrodynamic volume, and the presence of aggregates which is theassembly high molecular byproducts of the manufacturing process of thestarting manufacturing material of bovine hides, specifically Type 1collagen. The results of testing of prior Artifill® collagen samplesshowed a polydispersity and molecular weight distribution that containedmajority fractions, depending on sample tested, to be 40 to 80 percent(%) at approximately 100K daltons (Mw), or less. Additionally, Rz valuesfor the hydrodynamic radius showed three of the four Artifill® collagensamples tested with low numerical values indicating compacted threedimensional space occupation, such that influence of the low weightaverage molecular weight could be seen further differentiated from thehigher Mw sample tested. The tests further indicated single strandcomposition as part of the overall product make-up. The lowest Mwcomponent does not favorably influence stability or the strength of thecarrier gel properties and subsequent performance.

Avg. Molecular Calculated Weight (Mw) Mass by Astra Sample ID Gm/Mol kDRz μg Collagen (Knox 182K 45 197 gelatin) Artefill received in 183K 4953 50 cc syringed on Aug. 28, 2013 Lot# Artefill Collagen Lot# 241K 60216 F131056 received Oct. 11, 2013 (sample 5) Artefill Collagen Lot#104K 41 135 F131056 received Oct. 11, 2013 (sample 6)

Prior Art Artefill Collagen Sample 1- atelocollagen Number averagemolecular weight (Mn) 147 kDa Weight average molecular weight (Mw) 240kDa Polydispersity as Mw/Mn 1.638 % of molecular weights less than 100kDa 60% Prior Art Artefill Collagen Sample 2- atelocollagen Numberaverage molecular weight (Mn) 70 kDa Weight average molecular weight(Mw) 103.5 kDa Polydispersity as Mw/Mn 1.481 % of molecular weights lessthan 100 kDa 80% Gelatin sample- Knox gelatin 180-185 kDa (notdenatured) Number average molecular weight (Mn) 120 kDa Weight averagemolecular weight (Mw) 188 kDa Polydispersity as Mw/Mn 1.488 % ofmolecular weights less than 100 kDa <10%  Inventive Example- 3.5 wt %denatured atelocollagen Number average molecular weight (Mn) 151 kDaWeight average molecular weight (Mw) 183 kDa Polydispersity as Mw/Mn1.211 % of molecular weights less than 100 kDa 40%

The use of the terms “a” and “an” and “the” and similar referents(especially in the context of the following claims) are to be construedto cover both the singular and the plural, unless otherwise indicatedherein or clearly contradicted by context. The terms first, second etc.as used herein are not meant to denote any particular ordering, butsimply for convenience to denote a plurality of, for example, layers.The terms “comprising”, “having”, “including”, and “containing” are tobe construed as open-ended terms (i.e., meaning “including, but notlimited to”) unless otherwise noted. As used herein, wt % means percentby weight. Recitation of ranges of values are merely intended to serveas a shorthand method of referring individually to each separate valuefalling within the range, unless otherwise indicated herein, and eachseparate value is incorporated into the specification as if it wereindividually recited herein. The endpoints of all ranges are includedwithin the range and independently combinable. All methods describedherein can be performed in a suitable order unless otherwise indicatedherein or otherwise clearly contradicted by context. The use of any andall examples, or exemplary language (e.g., “such as”), is intendedmerely to better illustrate the invention and does not pose a limitationon the scope of the invention unless otherwise claimed. No language inthe specification should be construed as indicating any non-claimedelement as essential to the practice of the invention as used herein.

While the invention has been described with reference to an exemplaryembodiment, it will be understood by those skilled in the art thatvarious changes may be made and equivalents may be substituted forelements thereof without departing from the scope of the invention. Inaddition, many modifications may be made to adapt a particular situationor material to the teachings of the invention without departing from theessential scope thereof. Therefore, it is intended that the inventionnot be limited to the particular embodiment disclosed as the best modecontemplated for carrying out this invention, but that the inventionwill include all embodiments falling within the scope of the appendedclaims. Any combination of the above-described elements in all possiblevariations thereof is encompassed by the invention unless otherwiseindicated herein or otherwise clearly contradicted by context.

The invention claimed is:
 1. An alloplastic implant compositioncomprising microparticles having a diameter of about 5 to about 400 μmsuspended in an aqueous suspending agent, wherein the aqueous suspendingagent comprises denatured atelocollagen, wherein the denaturedatelocollagen has less than 10 wt % of the total weight as components ofweight average molecular weight (Mw) 100,000 Daltons or lower, andgreater than 70 wt % components of weight average molecular weight 100kDa to 258 kDa, wherein the polydispersity of the denaturedatelocollagen expressed as Mw/Mn is 1.0 to 1.6, wherein Mw is weightaverage molecular weight and Mn is number average molecular weight. 2.The alloplastic implant composition of claim 1, wherein the denaturedatelocollagen is prepared from bovine or porcine collagen.
 3. Thealloplastic implant composition of claim 1, wherein the pH of theaqueous suspending agent is 6.0 to 8.0 and the concentration ofdenatured atelocollagen in the aqueous suspending agent is 0.5 to 15 wt%.
 4. The alloplastic implant composition of claim 1, wherein themicroparticles have a diameter of about 10 to about 200 μm.
 5. Thealloplastic implant composition of claim 1, wherein the microparticlescomprise a polymer or copolymer comprising a methacrylate monomer. 6.The alloplastic implant composition of claim 5, wherein the polymer orcopolymer is polymethylmethacrylate.
 7. The alloplastic implantcomposition of claim 1, wherein the composition is injectable through a20 to 30 gauge needle.
 8. The alloplastic implant composition of claim1, further comprising an anesthetic.
 9. The alloplastic implantcomposition of claim 1, wherein the suspension is stable for at least 30days at a temperature of 20-25° C.